Controlled growth of β-Na 0.24V 2O 5 nanowire thin films

Jhih Syuan Ke, Ming Cheng Wu, Sheng Feng Weng, Chi-Shen Lee*

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

1 Scopus citations


A method to prepare well-aligned β-Na 0.24V 2O 5 nanowires (NWs) involves the deposition of a vanadium oxide complex onto a substrate via gaseous transport, followed by a reaction between the complex and a sodium cation (Na +) precursor coated on the substrate. Techniques to investigate the composition, crystallinity, and morphology of products as prepared include ICP-AES, X-ray powder diffraction (PXRD), SEM/transmission electron microscope (TEM), and XPS. PXRD patterns and images from a TEM confirm the single-crystalline nature of β-Na 0.24V 2O 5 NWs, which grow along direction [1 0 0]. Factors affecting the amount of deposited material and morphology were tested. On varying the reaction conditions, the length of the β-Na 0.24V 2O 5 wires is controlled in a range of 5-25 lm. A mechanism of formation is proposed. According to measurements of field emission, the turn-on field is 7.8 V/lm, and the maximum emission current density of 4.66 mA/cm 2 occurs at field 11 V/μm. This method is applicable to grow other tertiary metal oxide nanostructures on glass substrate.

Original languageEnglish
Article number1167
JournalJournal of Nanoparticle Research
Issue number10
StatePublished - 14 Sep 2012


  • Film
  • Morphology control
  • Nanowire
  • β-Na V O


Dive into the research topics of 'Controlled growth of β-Na 0.24V 2O 5 nanowire thin films'. Together they form a unique fingerprint.