Broadband Omnidirectional Light Trapping in Gold-Decorated ZnO Nanopillar Arrays

Yuan Ming Chang, Man Ling Lin, Tung Yen Lai, Chang Hung Chen, Hsin Yi Lee, Chih Ming Lin, Yew-Chuhg Wu, Yen Fu Lin*, Jenh-Yih Juang

*Corresponding author for this work

Research output: Contribution to journalArticlepeer-review

14 Scopus citations


The photoluminescence (PL) and reflectivity characteristics of zinc oxide nanopillars (ZnO-NPs) grown on indium-tin-oxide (ITO)-coated glasses were investigated. The room temperature PL showed bright white-light emission for the undoped ZnO-NPs grown at 600 °C, suggesting the close relation between the optical characteristic and the growth conditions being carried out for obtaining the present ZnO-NPs. The reflectivity of the as-grown ZnO-NPs array was about ∼29% with the wavelength of the incident light ranging from 200 to 1800 nm. Nevertheless, the reflectance reduced significantly to less than 9.9% when a layer of gold (Au) was deposited on ZnO-NPs by sputtering for 5 min, corresponding to more than 65% reduction in Au-coated ZnO-NPs (Au/ZnO-NPs). Moreover, the angle-resolved reflectance measurements on the present Au/ZnO-NPs array show an omnidirectional light-trapping characteristic. These remarkable characteristics, broadband and omnidirectional light-trapping of Au/ZnO-NPs, are attributed to the extended effective optical path of the incident light due to subwavelength scattering resulting from the presence of Au nanoparticles.

Original languageEnglish
Pages (from-to)11985-11992
Number of pages8
JournalACS Applied Materials and Interfaces
Issue number13
StatePublished - 5 Apr 2017


  • ZnO
  • broadband
  • light-trapping
  • omnidirectional
  • photoluminescence
  • white-light emission


Dive into the research topics of 'Broadband Omnidirectional Light Trapping in Gold-Decorated ZnO Nanopillar Arrays'. Together they form a unique fingerprint.

Cite this